Ultra premium

CPM S90V

The ultimate in wear resistance and edge retention comes with  CPM S90V steel. As you’d expect the carbon content is very high but the secret here is the extreme quantities of vanadium,

 

M390

M390 is one of the new super steels on the block,  It makes knife blades requiring excellent corrosion resistance and very high hardness for excellent wear resistance.  Chromium, molybdenum, vanadium, and tungsten are added to promote sharpness and edge retention.  M390 hardens to 60-62 HRC.

 

ZDP-189

ZDP-189 by Hitachi is another of the newer super steels containing huge quantities of carbon and chromium that result in ridiculous levels of hardness.  ZDP-189 averages around  64 HRC

 

Elmax

This is a high chromium-vanadium-molybdenum alloyed powdered steel with extremely high wear and corrosion resistance.

 

CTS-XHP

CTS-XHP  is another relatively new knife steel that has very good edge retention and hardens to about 61 HRC.  

 

Premium

CPM M4

CPM M4 provides superbly balances levels of abrasion resistancance and toughness through high doses of molybdenum (hence the “M”), vanadium and tungsten together with reasonably high levels of carbon.  It can be hardened to around 62-64 HRC

 

CPM S35VN

This is using a much finer grain structure and adding small quantities of niobium they were able to improve the toughness and ability to sharpen what was already an outstanding steel in the S30V.  

 

CPM S30V

CPM S30V (often simply referred to as S30V) steel has excellent edge retention and resists rust effortlessly. 

 

High end

154CM

A nice hard steel similar to S30V and is reasonably resistant to corrosion.  It has superb toughness good enough for most uses and holds an edge extremely well.  Moderately difficult to sharpen.  

 

ATS-34

it has very similar properties and characteristics to the 154CM, ATS-34 has great edge retention but is actually a little less rust resistant than the lower-range 440C steel.

 

D2

D2 steel is a tool steel often referred to as “semi-stainless” as it lacks the required amount of chromium (14%) to qualify as full stainless yet it still provides a good amount of resistance to corrosion. 

 

VG-10

The VG-10 steel is very similar to 154CM and ATS-34 with slightly more chromium but also contains vanadium which makes it marginally “better” than these two. 

 

H1

H1 steel from Japan’s Myodo Metals is basically the ultimate in corrosion resistance and essentially does not rust.  The epitome of true stainless steel.

 

N680

N680 steel contains about 0.20% nitrogen and over 17% chromium making it extremely corrosion resistant.  

 

Upper mid-range

440C

It’s reasonably tough and wear resistant but it really excels at stain resistance.  The 440C blades can be easily sharpened.  It has the highest levels of carbon and chromium in this group.

 

AUS-8
AUS-8 steel is Japanese made and like the 440C is highly resistant to rust and corrosion.  It’s also similarly tough but may not hold its edge as well as some of the more premium steels which carry a greater degree of carbon.  Real easy to sharpen. 

 

CTS-BD1

A vacuum-melted stainless steel is often likened to AUS-8 and 8Cr13MoV with many putting it slightly ahead of those two based on superior edge holding.  With slightly more chromium it also achieves better corrosion resistance.

 

8Cr13MoV

The MoV series of steels originate from China and comparable to AUS-8 but containing slightly higher carbon content.  

 

14C28N

The 14C28N stainless steel from Swedish manufacturer Sandvik is considered an upgrade to their 13C26 described below.

 

Lower mid-range

420HC

420HC is similar to 420 steel but with increased levels of carbon (HC stands for High Carbon) which makes the steel harder. That results in better edge retention and resistance to corrosion.  In fact, this is one of the most corrosion resistant steels out there,

 

440A

Very much like 420HC but with slightly more chromium which results in enhanced levels of wear resistance and edge retention but suffers from weaker anti-corrosion properties.

 

13C26

This is Sandvik’s version of the AEB-L steel, originally developed for razor blades.  Close comparison to 440A steel with a higher carbon to chromium ratio making it generally a little harder and wearable at the expense of corrosion resistance.  

 

Low end

420 & 420J

The 420 steel is a relatively low carbon content (usually less than 0.5%) which makes for a softer blade and as a result will tend to lose it’s edge quicker than higher end steels.   Blades made from 420 steel will rapidly lose their sharp edge over a relatively short time period. 

 

AUS-6

Japanese made equivalent to the 420 series steel.  Generally low quality and relatively little carbon content.

 

 

 

Tags: folding pocket knives,fixed blade knives, good multi tools